Polyurea crack filler

PP-CF Polyurea crack filler

PP-CF is a two parts, high penetration, fast setting, hybrid polyurea for repairing and re-building damaged concrete. The product is a 1:1 ratio, easy to mix system that is 98 % solids and VOC compliant. The PP-CF can be used to set anchor bolts, repair damaged control joints, fill spalling, and rebuild vertical curbing and steps. Sand or gravel can be added to extend the volume of the material and acts as filler for repairing large spalls, holes and cracks.

ADVANTAGES

  • Application temperature between 23°F to 100.4°F (-5°C to 38°C)
  • Product cures in 10 minutes @ 71.6°F (22°C) with excellent adhesion
  • Self-leveling and self-priming
  • Ready to service in 10 to 20 minutes
  • Easy to mix 1:1 ratio by volume
  • Highly chemical resistant
  • Excellent for industrial floor repairs subject to forklift traffic and harsh conditions

WHERE TO USE

  • Commercial freezer repairs
  • Aircraft hangar floors
  • Low temperature equipment
  • Maintenance facility floors
  • Garage floors
  • Industrial shop floors
  • Car washes or wash bays
  • Forming/ rebuilding stairs and steps
  • Leveling and grade matching
  • Bridge/ street repairs
  • Concrete polishing and other coating applications
  • Non-moving control joint fill

TECHNICAL DATA

IMPORTANT NOTE: PROPERTIES @ 73°F (23 °C) and 50% R.H. Times are approximate and will be affected by changing ambient conditions, especially changes in temperature and relative humidity. The indicated mileage is calculated for flat surfaces. A porous or imperfect surface will require more material in order to cover the same mileage.

PACKAGING 2 US gal kit (7.57 L)
COLOR PART A: Black
PART B: Amber
MIX (liquid/cured): Black/Grey
CURE TIME 10-15 minutes @ 71.6°F (22°C)
SHELF LIFE 12 months in original unopened factory sealed containers. Keep away from extreme cold, heat, or moisture. Keep out of direct sunlight and away from fire hazards.
MIX RATIO, BY VOLUME A:B = 1:1
MIX RATIO, BY WEIGHT A:B = 100:118
POT LIFE 3.5 OZ (100 G) 2-3 minutes @ 77°F (25°C)
DENSITY (KG/L) PART A: 0.94
PART B: 1.12
MIX: 1.11